Physicochemical Properties and Antibiofilm Activity of Tricalcium Silicate Cement and its Association with Cetrimide / Propiedades físico-químicas y actividad antibiofilm del cemento de silicato tricálcico y su asociación con cetrimida

Abstract Cetrimide (CTR) is a cationic surfactant detergent with antimicrobial and antibiofilm activity. The aim of this study was to evaluate setting time, pH, solubility and antibiofilm activity of tricalcium silicate cement (TSC) with zirconium oxide (ZrO2) and its association with 0.2 and 0.4% cetrimide. Initial and final setting times (IST and FST) were assessed based on ISO-6876. pH was evaluated at periods of 1,3,7,14 and 21 days. Solubility was analyzed by weight loss. A modified direct contact test (MDCT) on the biofilm of Enterococcus faecalis formed on bovine root dentin blocks was performed, after 6 hours of manipulation and 15 hours of contact time. The analysis was performed by UFC mL ¯¹ counting. The data were analyzed by ANOVA and Tukey's tests (α=0.05). Higher IST was observed for TSC/ZrO2+CTR in both concentrations than for TSC/ZrO2 and lower FST for TSC/ZrO2+0.4% CTR (p0.05). All materials exhibited increased mass. TSC/ZrO2+CTR 0.4% had lower mass gain than the other materials (p<0.05). The highest antibiofilm activity was observed for TSC/ZrO2+CTR in both concentrations, when compared with the positive control (p<0.05). In conclusion, CTR exhibited potential to promote greater antibiofilm activity to tricalcium silicate cement, without harming its physicochemical properties of setting time, pH and solubility.

Resumen Cetrimida (CTR) es un detergente y surfactante catiónico con actividad antimicrobiana y antibiofilm. El objetivo de este estudio fue evaluar el tiempo de fraguado, pH, solubilidad y actividad antibiofilm del cemento de silicato tricálcico (CST) con óxido de zirconio (ZrO2) y su asociación con CTR a 0.2% y 0.4%. Tiempo de fraguado inicial y final (TFI y TFF) fueron determinados con base en las normas ISO-6876. pH fue evaluado en los períodos de 1,3, 7,14 y 21 días. Solubilidad fue analizada por la pérdida de masa/peso. El test de contacto directo modificado (TCDM) fue realizado sobre biofilm de Enterococcus faecalis formado en dentina radicular bovina, después de 6 horas de manipulación de los cementos y 15 horas de contacto. El análisis fue realizado por la cuantificación de UFC mL¯¹. Los datos fueron analizados usando las pruebas de ANOVA y Tukey (α=0.05). Mayor TFI fue observado para CST/ ZrO2+CTR en las dos concentraciones que para TSC/ZrO2 y menor TFF para TSC/ ZrO2+CTR 0.4% (p0.05). Todos los materiales mostraron aumento de masa. TSC/ZrO2+CTR 0.4% tuvo menor gano de masa que los otros materiales (p<0.05). Mayor actividad antibiofilm fue observado para CST/ZrO2+CTR en las dos concentraciones, cuando comparados con el grupo control positivo (p<0.05). En conclusión, CTR demostró potencial para promover superior actividad antibiofilm al cemento de silicato tricálcico (CST), sin perjudicar sus propiedades físico-químicas de tiempo de fraguado, pH y solubilidad.

The influence of the particle's size on the setting reaction of sol-gel derived calcium silicate particles / A influência do tamanho de partícula na reação de presa de cimentos de silicate de cálcio produzidos por sol-gel

Introduction: This study aims to analyze the influence of particles size of sol-gel derived calcium silicate particles in the setting reaction of bioactive endodontic cements. Materials and Methods: Sol-gel derived calcium silicate particles were synthesized and sieved to separate the particles in different sizes: CS400, CS200, and CS100. A commercial MTA (Control) was used as control. The particle size and the specific surface area were assessed by laser diffraction and nitrogen adsorption. The cements were prepared with water as the liquid for the reaction. The setting time was conducted according to ISO 6876, and the setting kinetics was analyzed by Fourier trans-formed infrared spectroscopy (FTIR) at different time points between 120s to 72h. Results: The particle size varied from 9.45µm (CS400 ) to 31.01 (Control). The higher specific surface area valuer reached 15.14g/cm2 in the CS400. The smallest particle sizes, the higher specific surface area, and the lowest setting time were found for CS400 (p < 0.05). Control presented the highest setting time (p < 0.05). The FTIR analyses showed the differences in materials structure over time, with faster hydration and crystallization for CS400. The setting kinetics was slower for Control even when compared to a sol-gel derived group with similar particle size. Conclusion:The route of synthesis and the particle size influences the setting reaction of calcium silicate-based cements. The reduction of particle size for sol-gel derived calcium silicates lead to the acceleration of the setting reaction of the produced bioactive endodontic cement.

Introdução: Este estudo tem como objetivo analisar a influência do tamanho de partículas de silicato de cálcio derivadas de sol-gel na reação de presa de cimentos endodônticos bioativos. Materiais e Métodos: Partículas de silicato de cálcio derivadas de sol-gel foram sintetizadas e peneiradas para separar as partículas em diferentes tamanhos: CS400, CS200 e CS100. Um MTA comercial (Controle) foi usado como controle. O tamanho das partículas e a área superficial específica foram avaliados por difração a laser e adsorção de nitrogênio. Os cimentos foram preparados com água como líquido para a reação. O tempo de presa foi conduzido de acordo com a ISO 6876, e a cinética de presa foi analisada por espectroscopia de infravermelho transformada de Fourier (FTIR) em diferentes pontos de tempo entre 120s a 72h. Resultados: O tamanho de partícula variou entre 9,45µm (CS400) e 31,01 (Controle). A maior área de superfície foi encontrada nas partículas do grupo CS400 (15.14g/cm2). Os menores tamanhos de partícula, a maior área de superfície específica e o menor tempo de presa foram encontrados para CS400 (p < 0,05). O Control apresentou o maior tempo de presa (p < 0,05). As análises de FTIR mostraram as diferenças na estrutura dos materiais ao longo do tempo, com hidratação e cristalização mais rápidas para CS400. A cinética de presa foi mais lenta para Control mesmo quando comparado a um grupo derivado de sol-gel com tamanho de partícula semelhante. Conclusão: A rota de síntese e o tamanho das partículas influenciam a reação de endurecimento dos cimentos à base de silicato de cálcio. A redução do tamanho de partícula para silicatos de cálcio derivados de sol-gel leva à aceleração da reação de pega do cimento endodôntico bioativo produzido.

Radiopacity and Chemical Assessment of New Commercial Calcium Silicate-Based Cements / Radiopacidad y Evaluación Química de Cementos Comerciales en Base a Silicato de Calcio

ABSTRACT: The aim of the study was to evaluate the chemical composition and radiopacity of new calcium-silicatebased cements. Discs of 10 mm x 1 ± 0.1mm were prepared of BiodentineTM, TheraCal, Dycal and GC Fuji IX (n=5). The samples were radiographed directly on an PSP occlusal plate adjacent to an aluminium step wedge. The radiopacity of each specimen was determined according to ISO 9917/2007. Statistical analyses were carried out using ANOVA and Tukey's test at a significance level of 5 %. The chemical constitution of materials was determined by scanning electron microscopy (SEM) and energy dispersive x-ray element mapping. The radiopacities of the materials in decreasing order were: GC Fuji IX (3.45 ± 0.16 mm), Dycal (3.18 ± 0.17), BiodentineTM (2.79 ± 0.22), and TheraCal (2.17 ± 0.17). TheraCal showed the lowest radiopacity compared to the other materials, followed by BiodentineTM. Dycal and GC Fuji IX radiopacity values did not present significant statistical differences. Scanning electron microscopy and energy dispersive X-ray analysis revealed the presence of zirconium in BiodentineTM; and strontium, barium and zirconium in TheraCal as radiopacifying elements. The new calcium silicate cements present distinctive chemical composition. BiodentineTM contains zirconium as a radiopacifying element and has higher radiopacity values than TheraCal, which contains barium and strontium as radiopacifiers.

RESUMEN: El objetivo de este estudio fue evaluar la composición química y la radiopacidad de nuevos cementos en base a silicato de calcio. Discos de 10 mm x 1 ± 0,1 mm fueron preparados con BiodentineTM, TheraCal, Dycal y GC Fuji IX (n=5). Las muestras fueron radiografiadas directamente en una película PSP oclusal adyacente a una cuña escalonada de aluminio. La radiopacidad de cada espécimen fue determinada de acuerdo a la norma ISO 9917/ 2007. Se realizaron los análisis estadísticos con las pruebas ANOVA y test de Tukey con un nivel de significancia de 5 %. La constitución química de los materiales fue determinada con microscopía electrónica de barrido y con mapeo por análisis con dispersión de energía de rayos X. La radiopacidad de los materiales en orden decreciente fue: GC Fuji IX (3,45 ± 0,16 mm), Dycal (3,18 ± 0,7 mm), BiodentineTM (2,79 ± 0,22 mm), y TheraCal (2,17 ± 0,17 mm). TheraCal mostró la menor radiopacidad comparada con los otros materiales, seguido de BiodentineTM. Los valores de radiopacidad de Dycal y GC Fuji IX no presentaron diferencias estadísticas significativas. Los análisis de microscopía electrónica de barrido y mapeo por análisis con dispersión de energía de rayos X revelaron la presencia de zirconio en BiodentineTM; y de estroncio, bario y zirconio en TheraCal, como elementos radiopacos. Los nuevos cementos en base a silicato de calcio presentan una composición química distintiva. BiodentineTM contienen zirconio como elemento que provee radiopacidad y tiene mayor valor de radiopacidad que TheraCal, el cual contiene bario y estroncio como agente radiopaco.

Estudo do efeito da retençäo de corantes na translucidez do cimento de ionômero de vidro / The effect of translucense retention study of the glass ionomer cement

No presente estudo foi avaliado a traslucidez de novos cimentos de ionômero de vidro quando comparado ao cimento de silicato, levando-se em consideraçäo material, meios de imersäo e tempo. Os resultados mostraram que o cimento de silicato apresentava uma maior porcentagem de tranlucidez e que os corpos de prova imersos em soluçäo de café e coca-cola mostraram-se manchados, diminuindo assim a translucidez

Análise sobre o critério de utilizaçäo dos materiais (Parte II) / Analysis about linners use at brazilian dental schools (Part II)

Este trabalho permitiu o levantamento de dados relativos ao emprego dos materiais de proteçäo pulpar indicados pelas diferentes Faculdades de Odontologia do Brasil. Nesta segunda etapa, consideramos os critérios de proteçäo para os materiais restauradores estéticos (resina composta, cimento de silicato e cimento ionômero de vidro) e a análise das informaçöes colhidas permitiu concluir que para a situaçäo clínica mais simples (cavidade rasa) existe uma variaçäo entre as condutas adotadas para os dois primeiros materiais e unanimidade pela näo utilizaçäo de forradores sob o terceiro, quanto à situaçäo mais complexa (cavidade profunda) encontramos indicaçäo unânime para o emprego do cimento de hidróxido de cálcio sob todos os restauradores citados

Estudo espectrofotométrico da influência de certas bebidas na estabilidade de cor do cimento de silicato: In vitro / Spectrophometric study of the influence of certain drinks on the stability of the silicate cement color: in vitro

O objetivo desse trabalho é estudar "in vitro" o efeito de certas bebidas (chá, café e Coca-cola) na mudança de cor do cimento de silicato, observado longitudinalmente (6 idades), em duas marcas de cimento de silicato. A diferença de cor (delta E) foi obtida, de acordo com a norma CIE lab 76, e calculada a partir da reflectância fotométrica dos corpos de prova, na faixa de comprimento de onda da luz visível (400 e 740 nanômetros). Foi analisada ainda a importância da proteçäo inicial, com verniz nos corpos de prova, na sua estabilidade de cor. Pelos dados analisados, concluímos pela importância da proteçäo inicial na estabilidade de cor do cimento de silicato e influência dos fatores marca e tempo